ASTM B777-15 class2 tungsten alloy rod is produced by pressing and sintering metal powders into billets, which is worked by rolling or swaging into rod. Smaller sizes are produced by subsequent drawing. It is produced in straight random lengths with a smooth swaged surface at diameters 3mm and larger, and with a smooth drawn finish below 3mm. A centerless ground finish can also be furnished. Specific lengths and special fabrications can be supplied upon request.
The properties of ASTM B777-15 class2 tungsten alloy rod are:
Matrix: 92.5% W
Density: 17.15~17.85g/cc
Hardness Rockwell Max: 33HRC
Standard Alloy
Ultimate Tensile Strength: 110 KSI and 758 MPa
Yield Strength (0.2% offset): 75 KSI and 517 MPa
Elongation: 5%
Nonmagnetic Alloy
Ultimate Tensile Strength: 94 KSI and 648 MPa
Yield Strength (0.2% offset): 75 KSI and 517 MPa
Elongation: 2%